| About |
|---|
| Stat-Rite® M809 is a static dissipative acrylic alloy. Stat-Rite® M809 utilizes the patented Stat-Rite inherently dissipative polymer (IDP) alloy system to provide clean, permanent ESD protection. Stat-Rite® IDP alloys provide consistent static dissipation even when extruded, injection molded or thermoformed into components.&& |
| Product Description | |
|---|---|
| Supplier | Lubrizol Advanced Materials |
| Generic | SMMA |
| Material Status | Commercial: Active |
| Features | Good Clarity,Low (to None) Ion Content,Renewable resources,Electrostatic discharge protection,Moisture resistance,Antistatic property |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ASTM D792 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1450 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 27.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 30 | % | ASTM D638 |
| Bending modulus | 1450 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 140 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 75.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 67.0 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | |||
| — | 6.0E+9 | ohms | ESD S11.11 |
| — | 1.0E+10 | ohms | ASTM D257 |
| Volume resistivity | 4.0E+10 | ohms·cm | ASTM D257 |
| Electrostatic attenuation | |||
| +1000 V to 10 V | < 1.0 | sec |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Ion content | Internal Method | ||
| Anion Cl- | 20.0 | ng/cm² | Internal Method |
| Anion NO3- | 4.00 | ng/cm² | Internal Method |
| Anion PO4- | 15.0 | ng/cm² | Internal Method |
| Anion SO4- | 15.0 | ng/cm² | Internal Method |
| Cationic Na+ | 200 | ng/cm² | Internal Method |
| Outgassing | Internal Method | ||
| MMA | 40.0 | µg/g | Internal Method |
| Styrene | 15.0 | µg/g | Internal Method |
| Toluene | 180 | µg/g | Internal Method |
| Total Organics | 250 | µg/g | Internal Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 50% RH |
| 3. 12% RH |
| 4. CPM, 50% RH |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |