| About |
|---|
| AVP™ GLV8UCP是一种聚碳酸酯+聚丁烯对苯二甲酸酯（PC+PBT）产品,。 它可以通过注射成型进行加工,在北美洲有供货。 AVP™ GLV8UCP的应用领域包括电气/电子应用、家庭应用 和 汽车行业。 特性包括: 阻燃/额定火焰 环保/绿色 良好的抗紫外线能力 美观 耐冲击&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+PBT |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good surface appearance,High impact resistance,Good liquidity,Solvent resistance,HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 12 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.80 to 1.1 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 430 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.35 mm | 82.2 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.50 mm, black | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2000 | MPa | ASTM D638 |
| tensile strength | |||
| Yield, 3.18 mm | 46.9 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.18 mm | 25 | % | ASTM D638 |
| yield | 15 | % | ASTM D638 |
| Bending modulus | |||
| 3.18 mm | 2000 | MPa | ASTM D790 |
| bending strength | |||
| 3.18 mm | 70.3 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-grade, 3.18 mm | 112 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 | °C | |
| Drying time | 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended injection volume | 50 to 80 | % | |
| Barrel rear temperature | 238 to 254 | °C | |
| Barrel middle temperature | 243 to 260 | °C | |
| Barrel front temperature | 246 to 263 | °C | |
| Nozzle temperature | 243 to 260 | °C | |
| Processing (melt) temperature | 249 to 266 | °C | |
| Mold temperature | 38 to 82 | °C | |
| Back pressure | 0.172 to 0.345 | MPa | |
| Screw speed | 25 to 50 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |