| About |
|---|
| 30% glass fiber reinforced compound based on Polyamide 6&& |
| Product Description | |
|---|---|
| Supplier | A. Schulman |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good Dimensional Stability,Hydrolysis stability,Good liquidity,noise reduction,Low density,Grease resistance,Low moisture absorption,Low Gloss |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data |
|---|
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80.0 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.040 to 0.10 | % | |
| Proposed maximum recycled material ratio | 10 | % | |
| Hopper temperature | 70.0 | °C | |
| Barrel rear temperature | 230 | °C | |
| Barrel middle temperature | 240 | °C | |
| Barrel front temperature | 250 | °C | |
| Nozzle temperature | 260 | °C | |
| Processing (melt) temperature | 240 to 270 | °C | |
| Mold temperature | 60.0 to 90.0 | °C | |
| Injection pressure | 100 to 180 | MPa | |
| Injection speed | 快速 | ||
| Hold pressure | 50.0 to 110 | MPa | |
| Back pressure | 2.00 to 8.00 | MPa | |
| Cushion | 2.00 to 5.00 | mm | |
| Vent depth | 0.020 | mm | |
| Screw Speed | mm/sec | ||
| Notes |
|---|
| 1. International |
| 2. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |