| EMDA-6200 grade is a high-density polyethylene copolymer resin designed for blow molding small to medium size bottles. It can be used on intermittent as well as continuous blow molding machines for high-speed production of high quality bottles. The bottles have excellent environmental stress cracking resistance and a good balance of rigidity and impact strength. They are easily trimmed and exhibit excellent surface attributes. EMDA-6200 is intended for producing containers of up to 10 liter capacity for packaging household and industrial chemicals detergents, bleach, fabric softeners, etc.) toiletries, cosmetics and food products. It is also suitable for producing thin-walled parts and household items. In addition EMDA-6200 can also be used successfully for extruding sheets and profiles including corrugated drainage pipes.&& |
| Product Description | |
|---|---|
| Generic | HDPE copolymer |
| Material Status | Commercial: Active |
| Features | Good surface appearance,High impact resistance,Copolymer,High density,High ESCR |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.954 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，2.16kg | 0.40 | g/10min | ASTM D1238 |
| 190℃，21.6kg | 29 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| F50 | 50.0 | hr | ASTM D1693B |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 27.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 1100 | % | ASTM D638 |
| Bending modulus | 1250 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Resistance to drop impact | |||
| Mean Failure Height | 430.00 | cm | ASTM D2463 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 70.0 | ℃ | ASTM D648 |
| Embrittlement temperature | < -100 | ℃ | ASTM D746 |
| Vicat Softening Temp | 125 | ℃ | ASTM D1525 |
| Melting temperature | 135 | ℃ | Internal Method |
| Crystallization peak temperature | |||
| DSC | 112 | ℃ | Internal Method |
| Linear coefficient of thermal expansion | |||
| MD | 1.2E-4 | 1/℃ | ASTM D696 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Top Crushing Load at Failure（23℃） | 50000 | g | ASTM D2659 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 175 to 180 | °C | |
| Barrel 2 zone temperature | 185 to 190 | °C | |
| Barrel 3 zone temperature | 185 to 190 | °C | |
| Barrel 4 zone temperature | 185 to 190 | °C | |
| Connector temperature | 185 to 190 | °C | |
| Melt temperature | 200 to 215 | °C | |
| Nozzle temperature | 185 to 190 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 41g Boston Round quart (0.946 liter) bottle |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |