LITEN ML 71 - SOLIAO

About
LITEN ML 71 is a linear polyethylene, homopolymer with narrow molecular weight distribution and higher resistance to UV radiation, intended for injection moulding. It is suitable for manufacture of various types of crates, technical parts and other products for outdoor use requiring good rigidity, impact strength and resitance to warpage. LITEN ML 71 meets the hygienic requirements on materials and articles intended for contact with foodstuffs according to Regulation (EC) 1935/2004 of the European Parliament and of the Council, as well as according to Commission Regulation (EU) No 10/2011 including changes and additions.&&

About

LITEN ML 71 is a linear polyethylene, homopolymer with narrow molecular weight distribution and higher resistance to UV radiation, intended for injection moulding. It is suitable for manufacture of various types of crates, technical parts and other products for outdoor use requiring good rigidity, impact strength and resitance to warpage. LITEN ML 71 meets the hygienic requirements on materials and articles intended for contact with foodstuffs according to Regulation (EC) 1935/2004 of the European Parliament and of the Council, as well as according to Commission Regulation (EU) No 10/2011 including changes and additions.&&

Product Description
Generic	PE
Material Status	Commercial: Active
Features	Good Rigidity,Weather resistance is good,High impact resistance,High elastic,Food contact compliance,Weight distribution,Homopolymer
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.963	g/cm³	ISO 1183
Melt Flow Rate			ISO 1133
190℃，2.16kg	8.0	g/10min	ISO 1133
190℃，5.0kg	25	g/10min	ISO 1133
Shrinkage rate			ISO 294-4
TD	1.9	%	ISO 294-4
MD	3.5	%	ISO 294-4
ESCR(Environmental Stress Cracking Resistance)
55 ℃，F50	3.00	hr	ISO 22088
Melt flow ratio
21，6/2，16	25.0

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179
-30℃	5.5	kJ/m²	ISO 179
23℃	6.5	kJ/m²	ISO 179

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	45.0	℃	ISO 75-2/A
Vicat Softening Temp	126	℃	ISO 306
Melting temperature	136	℃	ISO 11357-3

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	58		ISO 868
Tensile modulus	1250	MPa	ISO 527-2
tensile strength
yield	25.0	MPa	ISO 527-2
Tensile strain
yield	8.5	%	ISO 527-2
Tensile creep modulus			ISO 899-1
1 hr	565	MPa	ISO 899-1
1000 hr	275	MPa	ISO 899-1
Bending modulus	1100	MPa	ISO 178

Process Conditions
injection	Nominal value	Unit	Test method
Processing (melt) temperature	200 to 260	°C
Mold temperature	20 to 60	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.