| LNP™ LUBRICOMP™ OFL36A compound LNP LUBRICOMP OFL36A is a compound based on PPS – Branched resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound OFL-4036 Product reorder name: OFL36A&&LNP™ LUBRICOMP™ OFL36A compound LNP LUBRICOMP OFL36A is a compound based on Polyphenylene Sulfide resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound OFL-4036 Product reorder name: OFL36A&&LNP™ LUBRICOMP™ OFL36A compound LNP LUBRICOMP* OFL36 is a compound based on PPS – Branched resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound OFL-4036 Product reorder name: OFL36A&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Lubricating,Branched polymer structure |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.69 | g/cm³ | ASTM D792 , ISO 1183 |
| Shrinkage rate | |||
| MD：24 hrs | 0.10 to 0.20 | % | ASTM D955 |
| TD：24 hrs | 0.30 to 0.50 | % | ASTM D955 |
| TD：24 hrs | 0.30 to 0.48 | % | ISO 294-4 |
| MD：24 hrs | 0.13 to 0.18 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.040 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 12300 | MPa | ASTM D638 |
| — | 11100 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 145 | MPa | ASTM D638 |
| fracture | 124 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 1.7 | % | ASTM D638 |
| fracture | 1.4 | % | ISO 527-2 |
| Bending modulus | 11000 | MPa | ASTM D790 , ISO 178 |
| bending strength | |||
| — | 200 | MPa | ASTM D790 |
| — | 197 | MPa | ISO 178 |
| friction coefficient | ASTM D3702 Modified | ||
| dynamic | 0.44 | ASTM D3702 Modified | |
| static state | 0.35 | ASTM D3702 Modified | |
| Wear factor | |||
| Washer | 33.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 85 | J/m | ASTM D256 |
| 23℃ | 9.4 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 550 | J/m | ASTM D4812 |
| 23℃ | 26 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak Load | 3.40 | J | ASTM D3763 |
| — | 1.97 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 269 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 266 | ℃ | ISO 75-2/Af |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 2.3E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 2.4E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 4.9E-5 | 1/℃ | ASTM E831 |
| TD：-40~40℃ | 5.0E-5 | 1/℃ | ISO 11359-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 to 149 | °C | |
| Drying time | 4.0 | hr | |
| Barrel rear temperature | 304 to 316 | °C | |
| Barrel middle temperature | 321 to 332 | °C | |
| Barrel front temperature | 332 to 343 | °C | |
| Processing (melt) temperature | 316 to 321 | °C | |
| Mold temperature | 138 to 166 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |