| Hepla® H7000 EX is a Polyamide 12 (Nylon 12) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for extrusion.Important attributes of:RoHS Compliant, Plasticized,Good Flexibility High Viscosity. |
| Product Description | |
|---|---|
| Supplier | NFD |
| Generic | PA12 |
| Material Status | Commercial: Active |
| Features | High Viscosity |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.03 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 1.3 | % | ISO 294-4 |
| MD | 0.9 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 1.4 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.7 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 4.2 | ISO 179/1eA | |
| 23℃ | 无断裂 | ISO 179/1eA | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 无断裂 | ISO 179/1eU | |
| 23℃ | 无断裂 | ISO 179/1eU |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.8 mm | HB | IEC 60695-11-10, -20 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.00E+13 | ohms | IEC 60093 |
| Volume resistivity | 1.00E+14 | ohms·cm | IEC 60093 |
| Dielectric strength | 32 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 95 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 45 | ℃ | ISO 75-2/A |
| Continuous use temperature | |||
| long-term | 80.0 to 100 | ℃ | ISO 2578 |
| short-term | 150 | ℃ | Internal Method |
| Melting temperature | 173 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD | 1.40E-04 | cm/cm/℃ | ISO 11359-2 |
| TD | 1.80E-04 | cm/cm/℃ | ISO 11359-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| D-level, 15 seconds | 65 | ISO 868 | |
| Tensile modulus | 472 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 31 | MPa | ISO 527-2 |
| fracture | 47 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 16 | % | ISO 527-2 |
| fracture | > 52 | % | ISO 527-2 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |