| Natural fibre reinforced compound for injection moulding.&& |
| Product Description | |
|---|---|
| Generic | 聚烯烃，共挤薄膜用聚烯烃 |
| Material Status | Commercial: Active |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.03 | g/cm³ | ISO 1183 |
| Apparent density | 0.46 | g/cm³ | ISO 60 |
| Melt Flow Rate | |||
| 230℃，5.0kg | 13 to 15 | g/10min | ISO 1133 |
| Shrinkage rate | 0.30 to 0.40 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3250 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| yield | 22.0 | MPa | ISO 527-2 |
| fracture | 22.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 3.0 | % | ISO 527-2 |
| Bending modulus | 3550 | MPa | ISO 178 |
| bending strength | |||
| 3.50% strain | 32.0 | MPa | ISO 178 |
| Bending strain | 4.0 | % | ISO 178 |
| Tensile Strain at Tensile Strength | 3.0 | % | ISO 527 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 3.3 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 7.9 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 139 | ℃ | ISO 306/A |
| Melting temperature | |||
| DSC | 150 to 180 | ℃ | ISO 3146 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.30 | % | |
| Barrel rear temperature | 150 | °C | |
| Barrel middle temperature | 170 | °C | |
| Barrel front temperature | 190 | °C | |
| Nozzle temperature | 200 | °C | |
| Mold temperature | 30 to 50 | °C | |
| Injection pressure | 200 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |