| A thermoset polyester composite that offers superior energy efficiency, temperature control, and durability for high temperature mold and platen thermal applications. A proven, cost effective product for the plastic and rubber molder. Available in thicknesses from 1/8″ – 2.00″. Color – Orange.&& |
| Product Description | |
|---|---|
| Generic | 热固性聚酯 |
| Material Status | Commercial: Active |
| Features | Durability |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Water absorption rate | |||
| Balance, 9.53 mm | 0.25 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 11000 | MPa | ASTM D638 |
| tensile strength | 82.7 | MPa | ASTM D638 |
| bending strength | 157 | MPa | ASTM D790 |
| compressive strength | ASTM D695 | ||
| — | 303 | MPa | ASTM D695 |
| 149℃ | 219 | MPa | ASTM D695 |
| 204℃ | 211 | MPa | ASTM D695 |
| 260℃ | 181 | MPa | ASTM D695 |
| Poisson’s ratio | 0.33 | ASTM E132 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 690 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Linear coefficient of thermal expansion | |||
| MD | 1.3E-5 | 1/℃ | ASTM D696 |
| Thermal conductivity coefficient | 1.9 | W/m/K | ASTM C177 |
| Maximum operating temperature | 288 | ℃ |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Cond. A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |