| About |
|---|
| Loyblend® HA-1700 is compounded blend of poly methyl methacrylate and acrylonitrile-butadiene-styrene. This grade offers high hardness, good scratch resistance and excellent weathering resistance with a good gloss surface&& |
| Product Description | |
|---|---|
| Generic | ABS+PMMA |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good surface appearance,High liquidity,Good Hardness,High scratch resistance,HB |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.09 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 20 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 230 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 4.0 mm | 86.0 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 114 | ASTM D785 | |
| tensile strength | 40.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 45 | % | ASTM D638 |
| Bending modulus | 2060 | MPa | ASTM D790 |
| bending strength | 60.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Barrel rear temperature | 190 to 200 | °C | |
| Barrel middle temperature | 195 to 205 | °C | |
| Barrel front temperature | 200 to 210 | °C | |
| Nozzle temperature | 210 to 220 | °C | |
| Mold temperature | 50 to 90 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |