| LL0220KJ is a linear low-density polyethylene copolymer with Butene-1 as the comonomer. LL0220KJ offers good mechanical and easy opening properties of the film. It is suitable for a wide variety of film applications and can be used as blend with LDPE. APPLICATIONS Hand Wrap Carrier and Garbage Bags Industrial Sacks Used as blend in LDPE&& |
| Product Description | |
|---|---|
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Smoothness,High anti-blocking,Inoxidizability,Copolymer,Butylene copolymer |
| Availabilitys | Africa & Middle East ,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.9 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | 0.10 | ISO 8295 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 38 | µm | |
| tensile strength | ISO 1184 | ||
| MD, yield, 38 µ m | 10.0 | MPa | ISO 1184 |
| TD, yield, 38 µ m | 11.0 | MPa | ISO 1184 |
| MD, fracture, 38 µ m | 33.0 | MPa | ISO 1184 |
| TD, fracture, 38 µ m | 25.0 | MPa | ISO 1184 |
| Tensile strain | ISO 1184 | ||
| MD, fracture, 38 µ m | 750 | % | ISO 1184 |
| TD, fracture, 38 µ m | 870 | % | ISO 1184 |
| Drop hammer impact | |||
| 38 µm | 130 | g | ISO 6603-2 |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD：38 µm | 1.8 | N | ISO 6383-2 |
| TD：38 µm | 4.9 | N | ISO 6383-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting peak temperature | 122 | ℃ | ASTM D2117 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45°，38 µm | 50 | ASTM D2457 | |
| Haze | |||
| 38 µm | 15 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |