| 30% CARBON FIBER REINFORCED, 13% PTFE/2% SILICONE LUBRICATED NYLON 6/12&& |
| Product Description | |
|---|---|
| Generic | PA 6/12 |
| Material Status | Commercial: Active |
| Features | Lubricating |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.20 to 0.40 | % | |
| Water absorption rate | ASTM D570 | ||
| 24hr | 0.10 | % | |
| saturated | 1.5 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 193 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 1.0 to 3.0 | % | ASTM D638 |
| Bending modulus | 19000 | MPa | ASTM D790 |
| bending strength | 306 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 91 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | 590 to 690 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 216 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 79.4 | °C | |
| Drying time | 4.0 | hr | |
| Processing (melt) temperature | 266 to 277 | °C | |
| Mold temperature | 93.3 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.013 to 0.025 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |