| Edgetek™ NY-20CF/000 BLACK is a Polyamide 6 (Nylon 6) product filled with carbon fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America.&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | PA6 |
| Material Status | Commercial: Negative |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.010 to 0.10 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 179 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.0 | % | ASTM D638 |
| Bending modulus | 12400 | MPa | ASTM D790 |
| bending strength | 248 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 6.4mm, injection molding | 53 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, annealed, 1.57 mm | 218 | ℃ | ASTM D648 |
| 1.8 MPa, annealed, 1.57 mm | 205 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+2 to 1.0E+4 | ohms | ASTM D257 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.10 to 0.20 | % | |
| Barrel rear temperature | 266 to 277 | °C | |
| Barrel middle temperature | 271 to 282 | °C | |
| Barrel front temperature | 277 to 288 | °C | |
| Nozzle temperature | 282 to 293 | °C | |
| Mold temperature | 49 to 71 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 0.20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |