| About |
|---|
| Aclar Flex 180 is a 18-micron (0.70-mil) CTFE homopolymer high performance barrier film for the pharmaceutical and medical markets. Its high barrier and excellent dimensional stability make it ideal for flexible packaging applications such as pouches, overwraps, and lidding.&& |
| Product Description | |
|---|---|
| Supplier | Honeywell |
| Generic | PCTFE |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good disinfection,Block resin |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 2.14 | g/cm³ | ISO 1183 |
| Apparent density | 1.16 | g/cm³ | ISO 60 |
| Melt Flow Rate | |||
| 288℃，2.16kg | 8.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ISO 527-2 | ||
| yield | 42.7 | MPa | |
| fracture | 26.2 | MPa | |
| Tensile strain | ISO 527-2 | ||
| yield | 7.0 | % | |
| fracture | 16 | % | |
| Bending modulus | 1600 | MPa | ISO 178 |
| bending strength | 61.0 | MPa | ISO 178 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Water vapor transmittance | |||
| 25 µm，38℃，100% RH | 0.25 | g·mm/m²/atm/24 hr | ASTM F1249 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 3.2 | kJ/m² | ISO 180 |
| Notched impact strength of cantilever beam | 74 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 104 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 75.0 | ℃ | ISO 75-2/A |
| Crystallization peak temperature | |||
| DSC | 214 | ℃ | ASTM D3418 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 25.4 µm | < 1.0 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |