AMPLIFY™ AA 698

About
AMPLIFY™ AA 698 is a medium acid copolymer offering enhanced adhesion vs. LDPE, and thus potential for reduced processing temperatures or processing without substrate or melt pre-treatments. Main Characteristics: Good adhesion to metallic, paper and PE Substrates Good heat sealability and hot-tack Excellent draw-down Low neck-in Complies with the requirements for use in contact with food of the EU-Directive 2002/72/EC. Contact a SK Sales office to obtain a detailed food contact compliance letter for this product. Complies with U.S. FDA 21 CFR 177.1310(b). Consult the regulations for complete details.&&

About

AMPLIFY™ AA 698 is a medium acid copolymer offering enhanced adhesion vs. LDPE, and thus potential for reduced processing temperatures or processing without substrate or melt pre-treatments. Main Characteristics: Good adhesion to metallic, paper and PE Substrates Good heat sealability and hot-tack Excellent draw-down Low neck-in Complies with the requirements for use in contact with food of the EU-Directive 2002/72/EC. Contact a SK Sales office to obtain a detailed food contact compliance letter for this product. Complies with U.S. FDA 21 CFR 177.1310(b). Consult the regulations for complete details.&&

Product Description
Supplier	DOW
Generic	EAA
Material Status	Commercial: Active
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.927	g/cm³	ASTM D792
Melt Flow Rate
190℃，2.16kg	7.5	g/10min	ASTM D1238
Co monomer content	3.0	%	Internal Method

MECHANICAL	Nominal value	Unit	Test method
tensile strength
Yield, molding	13.5	MPa
Fracture, molded	8.10	MPa
Tensile strain
Fracture, molded	490	%	ASTM D638

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	96.0	℃	ASTM D1525
Melting temperature
DSC	105	℃	Internal Method

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	260 to 310	°C
Shrinkage – 25 g/m2 at 100 m/min (290癈)	155.0	mm	Internal Method
Pulldown – Acceleration from 15 g/m2 at 100 m/min	150	m/min	Internal Method

Notes
1. Typical properties: these are not to be construed as specifications.
2. Comonomer content measured by direct titration procedure.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.