| EMERGE™ PC/ABS 7570EP高性能树脂是一款高流动的阻燃PC/ABS合金，不含氯、溴添加剂。该树脂特别适用于冷热模加工工艺，提供了优化的模具填充与保压性能。EMERGE PC/ABS 7570EP合适于广泛的信息技术设备与消费类电子行业。 应用领域： LCD电视外壳 显示器与PC外壳&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | High liquidity,Halogen free,Flame Characteristics,V-0 |
| Availabilitys | Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ISO 1183/B |
| Apparent density | 0.67 | g/cm³ | ISO 60 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 48 | g/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.39 to 0.43 | % | ISO 294-4 |
| MD | 0.41 to 0.46 | % | ISO 294-4 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 9.0 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 79.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 104 | ℃ | ISO 306/A120 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 35 | kV/mm | IEC 60243-1 |
| Dielectric constant | IEC 60250 | ||
| 100 Hz | 3.20 | IEC 60250 | |
| 1 MHz | 3.10 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 4.0E-3 | IEC 60250 | |
| 1 MHz | 7.0E-3 | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | V-0 | UL 94 | |
| Glowing wire flammability index | IEC 60695-2-12 | ||
| 1.0 mm | 960 | ℃ | IEC 60695-2-12 |
| 2.0 mm | 960 | ℃ | IEC 60695-2-12 |
| 3.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 1 mm | 800 | ℃ | IEC 60695-2-13 |
| 2 mm | 800 | ℃ | IEC 60695-2-13 |
| 3 mm | 800 | ℃ | IEC 60695-2-13 |
| Needle flame test | |||
| 1.50 mm | PASS | IEC 60695-2-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 120 | ISO 2039-2 | |
| Tensile modulus | 2740 | MPa | ISO 527-1-2 |
| tensile strength | ISO 527-2/50 | ||
| yield | 63.0 | MPa | ISO 527-2/50 |
| fracture | 49.0 | MPa | ISO 527-2/50 |
| Tensile strain | ISO 527-2/50 | ||
| yield | 3.9 | % | ISO 527-2/50 |
| fracture | 15 | % | ISO 527-2/50 |
| Bending modulus | 2700 | MPa | ISO 178 |
| bending strength | 92.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 85 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 230 to 280 | °C | |
| Mold temperature | 40 to 80 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |