| Polyamide 6.6 in black color reinforced with 25% of fiberglass, resistance to hydrolysis and UV. Good set of thermal properties, electrical and mechanical. Ideal for injection molding.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good Electrical Properties,Hydrolysis stability |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.49 | g/cm³ | ASTM D792 |
| Density | 1.53 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：24 hrs | 0.70 | % | ASTM D955 |
| MD：24 hrs | 0.20 | % | ASTM D955 |
| TD：24 hrs | 0.66 | % | ISO 294-4 |
| MD：24 hrs | 0.15 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 18600 | MPa | ASTM D638 |
| Tensile modulus | 19900 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 119 | MPa | ASTM D638 |
| fracture | 113 | MPa | ISO 527-2 |
| yield | 113 | MPa | ISO 527-2 |
| yield | 128 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 1.6 | % | ASTM D638 |
| fracture | 0.78 | % | ISO 527-2 |
| yield | 0.90 | % | ASTM D638 |
| yield | 0.77 | % | ISO 527-2 |
| Bending modulus | 20100 | MPa | ASTM D790 |
| Bending modulus | 19000 | MPa | ISO 178 |
| bending strength | 230 | MPa | ASTM D790 |
| bending strength | 176 | MPa | ISO 178 |
| friction coefficient | ASTM D3702 Modified | ||
| dynamic | 0.36 | ASTM D3702 Modified | |
| static state | 0.30 | ASTM D3702 Modified | |
| Wear factor | |||
| Washer | 15.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 320 | J/m | ASTM D4812 |
| 23℃ | 37 | J/m | ASTM D256 |
| 23℃ | 3.2 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 14 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak Load | 6.30 | J | ASTM D3763 |
| Multi axial instrumented impact energy | 1.50 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 248 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 259 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 272 | ℃ | ISO 75-2/Bf |
| 0.45 MPa, unannealed, 3.2 mm | 274 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 7.2E-6 | 1/℃ | ASTM E831 |
| TD：-40~40℃ | 7.0E-6 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 3.6E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 3.6E-5 | 1/℃ | ISO 11359-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 to 149 | °C | |
| Drying time | 4.0 | hr | |
| Barrel rear temperature | 304 to 316 | °C | |
| Barrel middle temperature | 321 to 332 | °C | |
| Barrel front temperature | 332 to 343 | °C | |
| Processing (melt) temperature | 316 to 321 | °C | |
| Mold temperature | 138 to 166 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |