| About |
|---|
| CALIBRE™ 891-10 Series provides superior ignition resistance in opaque applications. The CALIBRE 891-10 series products are available in 2 additive packages: CALIBRE 891: Mold release, CALIBRE 893: Mold release and UV stabilizer. Main Characteristics: Underwriters Laboratory Inc. (UL) Applications: Electronics Business equipment Appliances&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,V-0,5VA |
| Availabilitys | North America,Latin America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.20 | g/cm³ | ASTM D792，ISO 1183-A |
| — | 1.2 | g/cm³ | ISO 1183-3 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 10 | g/10min | ASTM D1238，ISO 1133 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 8.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| MD | 0.50 to 0.70 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，24hr | 0.15 | % | ASTM D570，ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA 3 | ||
| -30℃ | 15.0 | kJ/m² | ISO 179/1eA 3 |
| 23℃ | 30.0 | kJ/m² | ISO 179/1eA 3 |
| Charpy impact strength | ISO 179/1eU 3 | ||
| -30℃ | 无断裂 | ISO 179/1eU 3 | |
| 23℃ | 无断裂 | ISO 179/1eU 3 | |
| Impact strength of cantilever beam notch | |||
| 23℃ | 690 | J/m | ASTM D256 |
| 23℃ | 68 | kJ/m² | ISO 180-A |
| Dart impact equipped with measuring instruments | |||
| 23 ℃, total energy | 62.1 | J | ASTM D3763 |
| Tensile impact strength | 630 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa | 127 | ℃ | ISO 75-2 3 |
| Vicat Softening Temp | |||
| B50 | 151 | ℃ | ISO 306 3 |
| Linear coefficient of thermal expansion | |||
| MD | 7.0E-5 | 1/℃ | ISO 11359-2 3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.60 mm | V-0 | UL 94 | |
| 3.20 mm | V-0 | UL 94 | |
| Extreme oxygen index | 36 | % | ISO 4589-2 3 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | ||
| M-level | 59 | ASTM D785 | |
| R-level | 123 | ASTM D785 | |
| Tensile modulus | |||
| — | 2380 | MPa | ASTM D638 |
| — | 2380 | MPa | ISO 527-2/50 |
| — | 2300 | MPa | ISO 527-2 3 |
| tensile strength | |||
| yield | 61.4 | MPa | ASTM D638 |
| yield | 61.0 | MPa | ISO 527-2/50 |
| yield | 60.0 | MPa | ISO 527-2 3 |
| fracture | 58.6 | MPa | ASTM D638 |
| fracture | 59.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 6.0 | % | ISO 527-2 3 |
| fracture | 120 | % | ASTM D638 |
| fracture | 120 | % | ISO 527-2/50 |
| Tensile strain | |||
| fracture | > 50 | % | ISO 527-2 3 |
| Bending modulus | |||
| — | 2330 | MPa | ASTM D790 |
| — | 2330 | MPa | ISO 178 |
| bending strength | |||
| — | 97.9 | MPa | ASTM D790 |
| — | 98.0 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3. 2.0 in/min |
| 4. Method I (3 point load), 0.079 in/min |
| 5. 0.079 in/min |
| 6. 3-points |
| 7. 11.1 ft/sec |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |