| PLENCO 00714 is a melamine-phenolic copolymer molding compound, offering excellent arc resistance and comparative track index values. UL recognized under component file E40654. 00714 is available in brown. 00714 was qualified under military specification MIL-M-14 (superseded by ASTM D-5948) Type CMG and batches can, if requested and paid for, be tested for certification to the standard.&& |
| Product Description | |
|---|---|
| Generic | 三聚氰胺酚醛 |
| Material Status | Commercial: Active |
| Features | Arc resistance,Copolymer,V-0 |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.67 | g/cm³ | ASTM D792 |
| Apparent density | 0.70 | g/cm³ | ASTM D1895 |
| Shrinkage rate | |||
| MD | 0.36 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.22 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 21.8 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | 17 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 194 | ℃ | ASTM D648 |
| Continuous use temperature | 155 | ℃ | ASTM D794 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 7.5E+13 | ohms·cm | ASTM D257 |
| Dielectric strength | ASTM D149 | ||
| — | 14 | kV/mm | ASTM D149 |
| — | 10 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1 MHz | 6.50 | ASTM D150 | |
| Dissipation factor | |||
| 1 MHz | 0.047 | ASTM D150 | |
| Arc resistance | 186 | sec | ASTM D495 |
| Compared to the leakage tracing index | 425 | V | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| E-level | 74 | ASTM D785 | |
| Tensile modulus | 13300 | MPa | ASTM D638 |
| tensile strength | 59.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 0.80 | % | ASTM D638 |
| Bending modulus | 11200 | MPa | ASTM D790 |
| bending strength | 84.5 | MPa | ASTM D790 |
| compressive strength | 167 | MPa | ASTM D695 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 | °C | |
| Drying time | 0.50 | hr | |
| Mold temperature | 150 to 177 | °C | |
| Back pressure | 0.300 | MPa | |
| Screw speed | < 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method A (Short-Time) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |