PA6

About
Durethan® B30SF30 000000 PA 6, non-reinforced, injection molding, flame retardant&&Durethan® B30SF30 000000 PA 6, non-reinforced, injection molding, flame retardant&&Durethan® B30SF30 000000 PA 6, non-reinforced, injection molding, flame retardant&&

Product Description
Supplier	LANXESS
Generic	PA6
Material Status	Commercial: Active
Features	Flame Characteristics,V-0,5VA
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.35	g/cm³	ISO 1183
Shrinkage rate			ISO 2577
TD：260℃，2.0 mm	1.1	%	ISO 2577
TD：120℃，2.0 mm，4 hrs	0.40	%	ISO 2577
MD：260℃，2.0 mm	1.1	%	ISO 2577
MD：120℃，2.0 mm，4 hrs	0.40	%	ISO 2577

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
23℃	3600	MPa	ISO 527-1-2
tensile strength
Yield, 23 ℃	70.0	MPa	ISO 527-2/50
Tensile strain
Yield, 23 ℃	3.7	%	ISO 527-2/50
Nominal tensile fracture strain
23℃	9.0	%	ISO 527-2/50
Bending modulus
23℃	3200	MPa	ISO 178-A
bending strength			ISO 178/A
3.50% strain, 23 ℃	100	MPa	ISO 178-A
23℃	110	MPa	ISO 178-A
Bending strain	5.5	%	ISO 178/A

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179/1eA
-30℃	< 10	kJ/m²	ISO 179/1eA
23℃	< 10	kJ/m²	ISO 179/1eA
Charpy Unnotch Impact strength			ISO 179/1eU
-30℃	130	kJ/m²	ISO 179/1eU
23℃	150	kJ/m²	ISO 179/1eU
Impact strength of cantilever beam notch			ISO 180/1A
-30℃	< 10	kJ/m²	ISO 180-1A
23℃	< 10	kJ/m²	ISO 180-1A
Notched impact strength of cantilever beam			ISO 180/1U
-30℃	100	kJ/m²	ISO 180/1U
23℃	120	kJ/m²	ISO 180/1U

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	70.0	℃	ISO 75-2/A
Melting temperature	222	℃	ISO 11357-3

Electrical performance	Nominal value	Unit	Test method
Compared to the leakage tracing index
Solution A	300	V	IEC 60112

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level			UL 94
0.40 mm	V-0		UL 94
0.75 mm	V-0		UL 94
1.50 mm	V-0		UL 94
2.00 mm	5VA		UL 94
3.00 mm	5VA		UL 94
Glowing wire flammability index			IEC 60695-2-12
0.80 mm	960	℃	IEC 60695-2-12
1.5 mm	960	℃	IEC 60695-2-12
3.0 mm	960	℃	IEC 60695-2-12
Igniting temperature of the hot wire			IEC 60695-2-13
0.75 mm	825	℃	IEC 60695-2-13
1.5 mm	825	℃	IEC 60695-2-13
3 mm	800	℃	IEC 60695-2-13

Supplementary information	Nominal value	Unit	Test method
ISO Shortname	PA 6, GFHR, 14-040; ISO 1043-PA FR (17		ISO 1874

Process Conditions
injection	Nominal value	Unit	Test method
Drying Temperature – Dry Air Dryer	80	°C
Drying Time – Dry Air Dryer	2.0 to 6.0	hr
Processing (melt) temperature	250 to 270	°C
Mold temperature	80 to 100	°C
Admissible Residence Time at Tmax	> 10.0	min
Residual Moisture Content	0.030 to 0.12	%

Notes
1. Typical properties: these are not to be construed as specifications.
2. 60x60x2mm, 4 hr
3. 60x60x2mm, 80°C MT, 600 bar
4. 0.079 in/min
5. 2 mm/min
6. 10°C/min
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.