| About |
|---|
| NORYL™ Resin ZM3640 – Asia is a Polyphenylene Ether + PS (PPE+PS) product filled with mineral. It can be processed by injection molding and is available in Asia Pacific. Typical application: Electrical/Electronic Applications. Characteristics include: Flame Rated Flame Retardant Halogen Free Warp Resistant&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Low warping,Halogen free,Flame Characteristics,V-1 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，2.16kg | 24 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 60.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 4.0 | % | ASTM D638 |
| Bending modulus | |||
| 6.40 mm | 4620 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 6.40 mm | 102 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 35 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 103 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | ASTM E831 | ||
| MD：-40~40℃ | 4.2E-5 | 1/℃ | |
| TD：-40~40℃ | 4.8E-5 | 1/℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-1 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 87.8 to 93.3 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 30 to 70 | % | |
| Barrel rear temperature | 221 to 271 | °C | |
| Barrel middle temperature | 232 to 277 | °C | |
| Barrel front temperature | 243 to 282 | °C | |
| Nozzle temperature | 254 to 282 | °C | |
| Processing (melt) temperature | 254 to 282 | °C | |
| Mold temperature | 65.6 to 87.8 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Vent depth | 0.038 to 0.051 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 0.20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |