| Aquivion® E98-15S is a chemically-stabilized (denoted by S-suffix) perfluorosulfonic acid (PFSA) ionomer membrane that exhibits an Equivalent Weight (EW) of 980 g/eq. Nominal thickness is 150 microns. Aquivion® PFSA ionomer membranes are melt-extruded products based on the unique Short Side Chain copolymer of Tetrafluoroethylene (TFE) and Sulfonyl Fluoride Vinyl Ether (SFVE) F2C=CF-O-CF2CF2-SO2F produced by Solvay. They are available in the acid form and feature a lower Equivalent Weight (EW) than most commercial proton exchange membranes. The unique Short Side Chain copolymer allows higher crystallinity, improved mechanical properties and better proton conductivity. Typical applications include PEM fuel cells, water electrolyzers, separators for hydrogen or redox flow batteries, and pervaporation or gas humidification systems. Please visit Aquivion.com for more information.&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PFSA |
| Material Status | Commercial: Active |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| equivalent | |||
| EW | 980 | g/eq | Internal Method |
| Density | |||
| 50%R.H. | 1.930 | g/cm³ | Internal Method |
| membrane | |||
| thickness | 150.0 | µm | |
| weight | 290 | g/m² | |
| Total acidity | > 1.00 | meq/g | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D882 | ||
| MD, fracture | 40.0 | MPa | ASTM D882 |
| TD, fracture | 30.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture | 140 | MPa | ASTM D882 |
| TD, fracture | 175 | MPa | ASTM D882 |
| Tensile modulus | 290 | MPa |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Conductivity | > 160 | mS/cm | Internal Method |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Water absorption characteristics (liquid) | Internal Method | ||
| By weight | 30 | % | Internal Method |
| Tensile strain | |||
| TD | < 20 | % | Internal Method |
| MD, fracture | < 20 | % | Internal Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. eq = (mol SO3H) |
| 3. 23°C, 50% R.H. |
| 4. Measured on E98-05S at 23°C, 50% R.H. |
| 5. Setup: 4-probe, in-plane measurement; Procedure: set Tcell = 80°C, Tgas = 90°C, Humidity 100%, Flow 800 sccm. |
| 6. 4-hour soak in liquid at 100°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |