SABIC® HDPE PCG863

About
SABIC® HDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® HDPE PCG863 is typically used for the injection moulding of healthcare packaging, caps and closures and other parts for medical packaging. It is an easy-to-process, stiff grade. Compliance to regulations. SABIC® HDPE PCG863 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI).&&

About

SABIC® HDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® HDPE PCG863 is typically used for the injection moulding of healthcare packaging, caps and closures and other parts for medical packaging. It is an easy-to-process, stiff grade. Compliance to regulations. SABIC® HDPE PCG863 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI).&&

Product Description
Supplier	SABIC
Generic	HDPE
Material Status	Commercial: Active
Features	Good Rigidity,Excellent Processability,High purity,High density
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.963	g/cm³	ISO 1183
Melt Flow Rate			ISO 1133
190℃，2.16kg	8.0	g/10min	ISO 1133
190℃，5.0kg	23	g/10min	ISO 1133
ESCR(Environmental Stress Cracking Resistance)
40 ℃, 1.00 mm, 10% wetting agent, molded	8.00	hr	Internal Method

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23 ℃, molded	4.0	kJ/m²	ISO 180-A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	94.0	℃	ISO 75-2/B
Vicat Softening Temp	129	℃	ISO 306/A
Melting temperature
DSC	134	℃	ISO 11357-3
Enthalpy Change	226	J/g	ISO 11357-3

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D, molded	65		ISO 868
Tensile modulus
2 mm, molded into shape	1450	MPa	ISO 527-2/1BA/50
tensile strength			ISO 527-2/1BA/50
Yield, 2 mm, molded	31.0	MPa	ISO 527-2/1BA/50
Fracture, 2 mm, molded	15.0	MPa	ISO 527-2/1BA/50
Tensile strain
Fracture, 2 mm, molded	> 200	%	ISO 527-2/1BA/50
Bending modulus
2 mm, molded into shape	1650	MPa	ISO 178
bending strength
2 mm, molded into shape	32.0	MPa	ISO 178

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.