| Bormod HD915CF is a high cristallinity homopolymer film resin, based on special Borstar nucleating technology. This grade is specifically designed to be extruded as stiff core layer with a copolymer coat layer of Borclear RE718CF. This grade is suitable for the manufacturing of unoriented films for metallisation. Optical properties will not be deteriorated as with conventional homo or copolymers at these temperatures.&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Clarity,Good surface appearance,Renewable resources,Crystal,Optical performance,Nucleation,Low odor,High Heat Resistance,Homopolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 to 0.910 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 8.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Bending modulus | |||
| 23 ℃, injection molding | 2100 | MPa | ISO 178 |
| friction coefficient | |||
| With oneself – dynamic | 0.30 to 0.40 | ISO 8295 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| Membrane puncture force | |||
| 50 µm | 1.90 | N | ISO 7765-2 |
| Tensile modulus | ISO 527-3 | ||
| MD，50 µm | 1600 to 1800 | MPa | ISO 527-3 |
| TD，50 µm | 1600 to 1800 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD，50 µm | 35.0 to 55.0 | MPa | ISO 527-3 |
| TD，50 µm | 30.0 to 50.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 50 µ m | 80 to 120 | % | ISO 527-3 |
| TD, fracture, 50 µ m | 80 to 120 | % | ISO 527-3 |
| Dart impact equipped with measuring instruments | |||
| 50 µm，Total Energy | 800 | J | ISO 7765-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| A50 | 158 | ℃ | ISO 306/A50 |
| Melting temperature | |||
| DSC | 164 to 170 | ℃ | ISO 3146 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 20°，50 µm | > 90 | ASTM D2457 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |