| About |
|---|
| Jackdaw PC DS20WT6701是一种聚碳酸酯+聚丁烯对苯二甲酸酯（PC+PBT）产品,。 它,在欧洲有供货。 主要特性为:阻燃/额定火焰。&& |
| Product Description | |
|---|---|
| Generic | PC+PBT |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ASTM D792 , ISO 1183 |
| Water absorption rate | |||
| 24hr | 0.50 | % | ASTM D570 |
| 23℃，24hr | 0.50 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 65.0 | MPa | ISO 527-2 |
| — | 65.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 95 | % | ASTM D638 , ISO 527-2 |
| Bending modulus | 2200 | MPa | ASTM D790 , ISO 178 |
| bending strength | 90.0 | MPa | ASTM D790，ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 60 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 110 | ℃ | ASTM D648，ISO 75-2/B |
| 1.8 MPa, unannealed | 90.0 | ℃ | ASTM D648，ISO 75-2/A |
| Linear coefficient of thermal expansion | |||
| MD | 6.5E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+14 | ohms·cm | ASTM D257，IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 | |
| Extreme oxygen index | 25 | % | ASTM D2863，ISO 4589-2 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |