| Polyamide 6 in color blue with low viscosity (2.7), ideal for injection molding, good set of mechanical properties with excellent impact resistance and good heat resistance.&& |
| Product Description | |
|---|---|
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | High impact resistance,Low Viscosity,High Heat Resistance,HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 1.2 to 1.6 | % | ASTM D955 |
| Water absorption rate | |||
| balance | 1.3 | % | ASTM D570 |
| Relative viscosity | |||
| 98% sulfuric acid | 2.50 to 2.90 | ||
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 75.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 40 | % | ASTM D638 |
| Bending modulus | 3000 | MPa | ASTM D790 |
| bending strength | 100 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 55 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 66.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 205 | ℃ | ASTM D1525 2 |
| Melting temperature | 210 to 225 | ℃ | ASTM D2117 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 | hr | |
| Processing (melt) temperature | 210 to 230 | °C | |
| Mold temperature | 40 to 80 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |