| About |
|---|
| Standard flow Polyetherimide blend with low toxicity, smoke, and flame evolution. ECO Compliant, UL94 V0 listing.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polyetherimide |
| Material Status | Commercial: Active |
| Features | Low smoke,Low toxicity,ECO,V-0 |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.27 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 295℃，6.60kg | 1.6 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| TD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| MD：3.2 mm | 0.30 to 0.50 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3340 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 96.5 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 88 | % | ASTM D638 |
| Bending modulus | |||
| 100 mm span | 3210 | MPa | ASTM D790 |
| bending strength | |||
| Fracture, 100 mm span | 141 | MPa | ASTM D790 |
| Yield, 100 mm span | 145 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 80 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | |||
| 3.2mm | 2100 | J/m | ASTM D256 |
| Drop hammer impact | |||
| 23℃ | 35.3 | J | ASTM D3029 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 191 | ℃ | ASTM D648 |
| Relative temperature index | |||
| Electrical performance | 140 | ℃ | UL 746 |
| Strength mechanical performance | 140 | ℃ | UL 746 |
| Impact mechanical performance | 115 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Arc resistance | PLC 6 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 4 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 0 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 3 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 0 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | V-0 | UL 94 | |
| Halogen Content | 0 | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 135 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Drying time, maximum | 12 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 40 to 60 | % | |
| Barrel rear temperature | 310 to 332 | °C | |
| Barrel middle temperature | 321 to 343 | °C | |
| Barrel front temperature | 332 to 354 | °C | |
| Nozzle temperature | 327 to 349 | °C | |
| Processing (melt) temperature | 332 to 354 | °C | |
| Mold temperature | 93 to 135 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.025 to 0.076 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.10 in/min |
| 5. Tungsten Electrode |
| 6. Surface |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |