| Nypel 6030G HS BK is a 30% glass fiber reinforced, heat stabilized, black injection molding PA6 compound. Applications Nypel 6030G HS BK is generally recommended for applications such as bolts, racks, automotive underhood components, pressure regulator housings, caps and general industrial applications.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Heat Stabilized,HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 6.7 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 1.9 | % | ISO 62 |
| 23℃，24hr | 1.1 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | ||
| -40℃ | 8740 | MPa | ISO 527-2 |
| 23℃ | 9580 | MPa | ISO 527-2 |
| 80℃ | 3820 | MPa | ISO 527-2 |
| 120℃ | 2730 | MPa | ISO 527-2 |
| 150℃ | 2890 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| Fracture, -40 ℃ | 220 | MPa | ISO 527-2 |
| Fracture, 23 ℃ | 155 | MPa | ISO 527-2 |
| Fracture, 80 ℃ | 80.0 | MPa | ISO 527-2 |
| Fracture, 120 ℃ | 65.0 | MPa | ISO 527-2 |
| Fracture, 150 ℃ | 60.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.0 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 8070 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 230 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 8.6 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | 54 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | ISO 180 | ||
| -40℃ | 6.5 | kJ/m² | ISO 180 |
| 23℃ | 8.0 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 205 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 219 | ℃ | ISO 75-2/B |
| Melting temperature | |||
| DSC | 220 | ℃ | ISO 3146 |
| Linear coefficient of thermal expansion | |||
| TD | 6.7E-5 | 1/℃ | |
| MD | 2.5E-5 | 1/℃ | |
| 0.8 mm | 130 | ℃ | UL 746 |
| 1.5 mm | 140 | ℃ | UL 746 |
| 3.0 mm | 140 | ℃ | UL 746 |
| Relative temperature index | |||
| Electrical performance | UL 746 | ||
| Strength mechanical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| 0.8 mm | 115 | ℃ | UL 746 |
| 1.5 mm | 115 | ℃ | UL 746 |
| 3.0 mm | 120 | ℃ | UL 746 |
| 0.8 mm | 130 | ℃ | UL 746 |
| 1.5 mm | 140 | ℃ | UL 746 |
| 3.0 mm | 140 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.80 mm | HB | UL 94 | |
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 83 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Processing (melt) temperature | 270 to 295 | °C | |
| Mold temperature | 80 to 95 | °C | |
| Injection pressure | 3.50 to 12.5 | MPa | |
| Injection speed | Fast | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |