| TN2006 is an Ethylene-Vinyl Acetate (EVA) copolymer with good mechanical properties, high flexibility and toughness even at low temperatures. It has excellent optical and heat sealability properties. Additionally, this product has good water vapor barrier. The rheological properties allow processability in tubular film extrusion equipment, being able to be coextruded in combination with many other materials. Additives Antioxidant Application: Heat seal layer in coextruded and laminated films. Food packaging. Hood stretch films. Base polymer for agricultural films. Geomembranes.&& |
| Product Description | |
|---|---|
| Supplier | Braskem |
| Generic | EVA |
| Material Status | Commercial: Active |
| Features | Good flexibility,Good heat sealing,Optical performance,Moisture resistance,Inoxidizability,Ultra high toughness,Copolymer,Low temperature toughness |
| Availabilitys | Latin America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.940 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.70 | g/10min | ASTM D1238 |
| Vinyl acetate content | 18.0 | wt% | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shaw A, molded | 89 | ASTM D2240 | |
| Shaw’s D, molded | 39 | ASTM D2240 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | |||
| 2% secant, TD, 50 µ m, blow molded film | 38.0 | MPa | ASTM D882 |
| 2% secant, MD, 50 µ m, blow molded film | 39.0 | MPa | ASTM D882 |
| tensile strength | |||
| Fracture, molded | 33.0 | MPa | ASTM D638 |
| TD, fracture, 50 µ m, blow molded film | 33.0 | MPa | ASTM D882 |
| MD, fracture, 50 µ m, blow molded film | 38.0 | MPa | ASTM D882 |
| Tensile strain | |||
| Fracture, molded | 680 | % | ASTM D638 |
| TD, fracture, 50 µ m, blow molded film | 700 | % | ASTM D882 |
| MD, fracture, 50 µ m, blow molded film | 820 | % | ASTM D882 |
| Drop hammer impact | |||
| 50 µ m, blow molded film | 950 | g | ASTM D1709-B |
| tear strength | |||
| TD, 50 µ m, blow molded film | 320 | g | ASTM D1922 |
| MD, 50 µ m, blow molded film | 210 | g | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 70.0 | ℃ | ASTM D1525 2 |
| Melting peak temperature | 90.0 | ℃ | ASTM D3418 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 50.0 µ m, blow molded film | 92 | ASTM D2457 | |
| Haze | |||
| 50 µ m, blow molded film | 2.0 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |