| About |
|---|
| Product Description Phenolic moulding compound, inorganically/organically filled, average heat resistance, increased dimensional stability, dishwasher proof, UL listed moulding compound 1.5 mm / V-0 (ALL) Application Areas MCB-housings, cookware fittings, knobs, handles&& |
| Product Description | |
|---|---|
| Generic | 酚醛树脂 |
| Material Status | Commercial: Active |
| Features | Good surface appearance,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.47 | g/cm³ | ISO 1183 |
| Apparent density | 0.65 | g/cm³ | ISO 60 |
| Shrinkage rate | ISO 2577 | ||
| — | 0.75 | % | ISO 2577 |
| Water absorption rate | |||
| 23℃，24hr | 45.0 | mg | ISO 62 |
| Post contraction | ISO 2577 | ||
| — | 0.45 | % | ISO 2577 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 1.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 7.0 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 8.0 MPa, unannealed | 125 | ℃ | ISO 75-2/C |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+10 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+11 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 1 mm | 25 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 100 Hz | 9.50 | IEC 60250 | |
| Dissipation factor | |||
| 100 Hz | 0.25 | IEC 60250 | |
| Compared to the leakage tracing index | |||
| Solution A | 125 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.50 mm, all colors | V-0 | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Compression molding pressure | > 15.0 | MPa | |
| Compression molding temperature | 160 to 190 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H 961/30 | 340 | MPa | ISO 2039-1 |
| Tensile modulus | 7500 | MPa | ISO 527-1-2 |
| tensile strength | 55.0 | MPa | ISO 527-2/5 |
| Bending modulus | 8000 | MPa | ISO 178 |
| bending strength | 95.0 | MPa | ISO 178 |
| compressive strength | 250 | MPa | ISO 604 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Barrel rear temperature | 60 to 75 | °C | |
| Nozzle temperature | 80 to 100 | °C | |
| Processing (melt) temperature | 80 to 100 | °C | |
| Mold temperature | 160 to 190 | °C | |
| Injection pressure | > 15.0 | MPa | |
| Back pressure | 0.500 to 2.00 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Compression |
| 3. Injection |
| 4. 0.079 in/min |
| 5. short term, electrode layout P25mm/P25mm in transformer oil equivalent to IEC 60296 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |