| About |
|---|
| H 117 is a ultra-high melt flow rate homopolymer. This product is suitable to high productivity on thin-walled parts. H 117 features an excellent stiffness, thermal resistance, low warpage parts, easy mould filling and high speed injection moulding. Applications: Thin-walled parts; Media Packaging; Housewares. Processing: Injection Moulding&& |
| Product Description | |
|---|---|
| Supplier | Braskem |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low warping,High liquidity,Quick molding cycle,Heat Stabilized,Homopolymer |
| Availabilitys | Latin America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.905 | g/cm³ | ASTM D792 |
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 45 | g/10min | ISO 1133 |
| 230℃，2.16kg | 45 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, injection molding | 20 | J/m | ASTM D256 |
| 23 ℃, injection molding | 2.6 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, injection molded | 65.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 65.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed, injection molded | 123 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 121 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 155 | ℃ | ASTM D1525 3 |
| Vicat Softening Temp | 155 | ℃ | ISO 306/A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, injection molding | 38.0 | MPa | ISO 527-2 |
| Yield, injection molding | 38.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Yield, injection molding | 7.0 | % | ASTM D638 |
| Yield, injection molding | 9.0 | % | ISO 527-2 |
| Bending modulus | |||
| 1% cut, injection molding | 1700 | MPa | ISO 178 |
| 1% cut, injection molding | 1700 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 102 | ISO 2039-2 | |
| R-level | 105 | ASTM D785 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Injection Molded |
| 3. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |