| Sup-tech A706SH is a Polyamide product filled with 30% glass fiber. It can be processed by injection molding and is available in Asia Pacific. Primary characteristic: flame rated.&& |
| Product Description | |
|---|---|
| Supplier | Suptech |
| Generic | PA Not specified |
| Material Status | Commercial: Negative |
| Features | HB |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 | g/cm³ | DIN 53479 |
| Shrinkage rate | 2.0E-3 to 6.0E-3 | % | DIN 53464 |
| Water absorption rate | DIN 53495 | ||
| 23℃，24hr | 0.80 | % | DIN 53495 |
| Saturation, 23 ℃ | 5.0 | % | DIN 53495 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 13 | kJ/m² | DIN 53453 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | DIN 53461 | ||
| 0.45 MPa, unannealed | 258 | ℃ | DIN 53461 |
| 1.8 MPa, unannealed | 250 | ℃ | DIN 53461 |
| Melting temperature | 260 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+12 | ohms | IEC 60093 |
| Dielectric strength | 20 | kV/mm | DIN 53481 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 119 | ISO 2039-2 | |
| tensile strength | |||
| fracture | 160 | MPa | DIN 53455 |
| Tensile strain | |||
| fracture | 3.0 | % | DIN 53452 |
| Bending modulus | 8000 | MPa | DIN 53457 |
| bending strength | 210 | MPa | DIN 53457 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 | °C | |
| Drying time | 6.0 to 10 | hr | |
| Processing (melt) temperature | 260 to 300 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |