| About |
|---|
| Product Description | |
|---|---|
| Generic | PVC alloy |
| Material Status | Commercial: Active |
| Features | High liquidity,low-temperature impact resistance |
| Availabilitys | Asia Pacific,Europe,Latin America,Africa & Middle East ,North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.31 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.4 | % | ASTM D995 |
| TD | 0.6 | % | ASTM D995 |
| Spiral flow | 86.4 | cm | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 屈服，51 mm/min，23°C | 41.4 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | |||
| Tensile modulus | |||
| 23℃，51 mm/min | 2410 | MPa | ASTM D638 |
| bending strength | |||
| 23℃ | 69.6 | MPa | ASTM D790 |
| Bending modulus | |||
| 23℃ | 2620 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, annealed | 82.2 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 76.1 | ℃ | ASTM D648 |
| 1.8 MPa, annealed | 78.9 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 72.2 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 9.0E-5 | 1/℃ | ASTM D696 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50mm | V-0，5VA | UL 94 | |
| 3.00mm | V-0，5VA | UL 94 |
| Other performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Regional availability | 非洲和中东，亚太地区，欧洲，北美，南美 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 107 | J/m | ASTM D256-A |
| Impact strength of cantilever beam notch | |||
| 23℃ | 801 | J/m | ASTM D256 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |