| FREQTIS® P0833A是一种聚苯硫醚(PPS)产品,含有的填充物为60% 矿物填料。 它,在北美洲、欧洲或亚太地区有供货。 主要特性为:阻燃/额定火焰。&& |
| Product Description | |
|---|---|
| Supplier | Polyplastics |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | 115 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 0.80 | % | ISO 527-2 |
| Bending modulus | 18000 | MPa | ISO 178 |
| bending strength | 165 | MPa | ISO 178 |
| Bending strain | 0.90 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 2.3 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Linear coefficient of thermal expansion | Internal Method | ||
| MD | 2.0E-5 | 1/℃ | Internal Method |
| TD | 3.0E-5 | 1/℃ | Internal Method |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 3.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 3 mm | 12 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 1 MHz | 8.00 | IEC 60250 | |
| 3.00 GHz | 8.00 | Internal Method | |
| Dissipation factor | |||
| 3 GHz | 3.0E-3 | Internal Method | |
| Arc resistance | 159 | sec | |
| Compared to the leakage tracing index | 175 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Color Number | KD3051 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 2.12 | g/cm³ | ISO 1183 |
| Shrinkage rate | Internal Method | ||
| TD：2.0 mm | 0.60 | % | Internal Method |
| MD：2.0 mm | 0.30 | % | Internal Method |
| Water absorption rate | |||
| 23℃，24hr | 0.010 | % | ISO 62 |
| Apparent viscosity of melt | |||
| 310℃，1000 sec^-1 | 290000 | mPa·s | ISO 11443 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |