| About |
|---|
| UPES® 315-LR是一种聚本乙烯+ PE (PS+PE)材料,。 该产品在北美洲有供货,。&& |
| Product Description | |
|---|---|
| Generic | PS+PE |
| Material Status | Commercial: Active |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.02 | g/cm³ | ASTM D6226 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 0.35 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| injection molding | 2220 | MPa | ASTM D638 |
| tensile strength | |||
| Fracture, injection molding | 36.8 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, injection molding | 3.3 | % | ASTM D638 |
| Bending modulus | |||
| injection molding | 1800 | MPa | ASTM D790 |
| bending strength | |||
| Yield, injection molding | 53.8 | MPa | ASTM D790 |
| Bending strain | |||
| yield | > 5.1 | % | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| Injection molding | 23 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 101 | ℃ | ASTM D1525 6 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Shrinkage rate | ASTM D955 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |