| 15 MFI Flame Retardant, with UV and Release, Non-chlorine non-bromine FR system, RoHS compliant Application/Use: Injection molded housings and components of communications equipment, electronics and electrical devices, appliances. Key Words: Polymer; Thermoplastic; Polycarbonate (PC); Polycarbonate, Unreinforced, Non chlorine Non Bromine Flame Retardant, Impact Modified&& |
| Product Description | |
|---|---|
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Halogen free,Good stripping performance,Flame Characteristics |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.23 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 15 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| Outdoor applicability | f1 | UL 746C | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 750 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 137 | ℃ | |
| 1.8 MPa, unannealed | 127 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD：-40~95℃ | 7.0E-5 | 1/℃ | |
| TD：-40~95℃ | 6.8E-5 | 1/℃ | |
| Relative temperature index | 125 | ℃ | UL 746 |
| Electrical performance | 125 | ℃ | UL 746 |
| Impact mechanical performance | 115 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 23℃ | 6.0E+15 | ohms·cm | |
| 90 ℃ | 3.0E+15 | ohms·cm | |
| Dielectric strength | |||
| 3.18 mm | 24 | kV/mm | ASTM D149 |
| Arc resistance | PLC 6 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 2 | UL 746 | |
| High Arc Burning Index (HAI) | |||
| 1.5 mm | PLC 0 | ||
| 3.0 mm | PLC 1 | ||
| High voltage arc marking rate | |||
| HVTR | PLC 3 | UL 746 | |
| Hot wire ignition | |||
| HWI | |||
| 1.5 mm | PLC 3 | ||
| 3.0 mm | PLC 2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | ||
| 2.50 mm, black, gray, brown | |||
| 3.00 mm, all colors | |||
| Glowing wire flammability index | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | 775 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 37 | % | ASTM D2863 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| UL Rating | |||
| Non-bromine，Non-chlorine | Pass | UL 746H | |
| RoHS Compliance | Pass | UL 746R |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 120 | ASTM D785 | |
| tensile strength | |||
| Yield, 3.17 mm | 55.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.17 mm | 75 | % | ASTM D638 |
| Bending modulus | |||
| 3.17 mm | 2070 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 3.17 mm | 86.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 48 | hr | |
| Recommended injection volume | 40 to 60 | % | |
| Barrel rear temperature | 249 to 271 | °C | |
| Barrel middle temperature | 260 to 271 | °C | |
| Barrel front temperature | 271 to 288 | °C | |
| Nozzle temperature | 266 to 282 | °C | |
| Processing (melt) temperature | 277 to 293 | °C | |
| Mold temperature | 71 to 93 | °C | |
| Injection pressure | 68.9 to 124 | MPa | |
| Back pressure | 0.345 to 1.38 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Clamping force | 2.8 to 6.9 | kN/cm² | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 40 hr @ 50% RH |
| 3. 96 hr @ 50% RH |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |