| About |
|---|
| Advanced Composites ATX832N is a Compounded Polypropylene product filled with talc. It is available in North America. Typical application: Automotive. Characteristics include: High Flow Impact Resistant Scratch Resistant&& |
| Product Description | |
|---|---|
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Features | High impact resistance,High liquidity,High scratch resistance |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Flow Rate | 30 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| 3.0 mm | 9.0E-3 to 0.011 | % | ISO 294-4 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180 | ||
| -40℃ | 5.0 | kJ/m² | ISO 180 |
| 23℃ | 28 | kJ/m² | ISO 180 |
| Dart impact equipped with measuring instruments | |||
| 0℃ | 36.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 123 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 64.0 | ℃ | ISO 75-2/A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 59 | ISO 868 | |
| tensile strength | |||
| yield | 25.0 | MPa | ISO 527-2 |
| Bending modulus | 2180 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 204 | °C | |
| Barrel middle temperature | 218 | °C | |
| Barrel front temperature | 218 | °C | |
| Nozzle temperature | 216 | °C | |
| Processing (melt) temperature | 204 to 232 | °C | |
| Mold temperature | 32 to 49 | °C | |
| Cushion | 6.35 to 12.7 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 22.0 ft/sec |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |