| Hostacom SD068-4C fractional melt flow, 2,000 MPa flexural modulus, 40% calcium filled polypropylene copolymer is designed for blow molding and extrusion. This material is characterized by very good melt strength, excellent processability and an excellent impact/stiffness balance. Typical applications include wiring channels, ductwork and seat backs.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | HMS PP |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Low liquidity,High impact resistance,Good melt strength,Copolymer |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.23 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 0.40 | g/10min | ISO 1133 |
| 230℃，2.16kg | 0.40 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 23.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 300 | % | ISO 527-2 |
| Bending modulus | 2000 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 55 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 97.0 | ℃ | ISO 75-2/B |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |