| About |
|---|
| HIPREN® EM 1500 T is produced by cold copolymerisation process, with the use of rosin acids soaps as emulsifiers, and contains 23.5% styrene bounded in polymer. The rubber is stabilised with staining antioxidant added during the production process. HIPREN® EM 1500T is dark coloured, without nitrosoamine. HIPREN® EM 1500 T is compatible with natural rubber and other synthetic rubbers. Good compatibility, easy incorporation of various compounding ingredients provide possibility of mixing formulations for different applications requirement. Application: HIPREN EM 1500 T is used for production of wide range products including simple small articles, moulded and pressed products, light pneumatics and heavy conveyer belts, hoses, tires etc.&& |
| Product Description | |
|---|---|
| Generic | SBR-乳液聚合 |
| Material Status | Commercial: Active |
| Features | Inoxidizability |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Mooney viscosity | |||
| ML 1+4，100℃ | 51 | MU | ISO 289 |
| Combined with styrene | 23.5 | % | ISO 2453 |
| Organic Acid | 6.6 | wt% | ISO 7781 |
| Soap | 0.5 | wt% | ISO 7781 |
| Stabilizer | 0.4 | wt% | |
| Ash Content | 0.4 | % | ISO 247 |
| Volatiles | 0.50 | wt% | ISO 248 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 63 to 71 | ISO 868 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, 145 ℃ | > 23.0 | MPa | ISO 37 |
| 300% strain, 145 ℃ | 11.7 to 16.7 | MPa | ISO 37 |
| Tensile strain | |||
| Fracture, 145 ℃ | > 400 | % | ISO 37 |
| Basho’s elasticity | > 40 | % | ISO 4662 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 91.5 | ℃ | ASTM D1525 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Curing time | ISO 6502 | ||
| 50% | 7.5 to 11.5 | min | ISO 6502 |
| 90% | 14.2 to 19.2 | min | ISO 6502 |
| Coking time | 2.9 to 4.9 | min | ISO 6502 |
| Torque | ISO 6502 | ||
| Max | 19.0 to 23.0 | dNm | ISO 6502 |
| Min | 2.00 to 3.00 | dNm | ISO 6502 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Vulcanization temperature 145°C; Vulcanization time 35 min; Test specimen SI |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |