DINALEN® 65 - SOLIAO

About
DINALEN® 65 is low density polyethylene containing slip and anti-blocking additives. It is intended for thin blow film extrusion. Other processing techniques can be used in less extent. DINALEN® 65 exhibits excellent processability, uniform optical and other properties, depending on its application. It is extruded at temperatures ranging from 140°C to 165°C. DINALEN® 65 gives films of desired properties depending on selected processing parameters such as processing temperature and capacity; blowing ratio, and the height of the frost line. Recommended film thickness : 0.020 mm to 0.040 mm.&&

About

DINALEN® 65 is low density polyethylene containing slip and anti-blocking additives. It is intended for thin blow film extrusion. Other processing techniques can be used in less extent. DINALEN® 65 exhibits excellent processability, uniform optical and other properties, depending on its application. It is extruded at temperatures ranging from 140°C to 165°C. DINALEN® 65 gives films of desired properties depending on selected processing parameters such as processing temperature and capacity; blowing ratio, and the height of the frost line. Recommended film thickness : 0.020 mm to 0.040 mm.&&

Product Description
Generic	LDPE
Material Status	Commercial: Active
Features	Excellent Processability,Good Clarity,Good surface appearance,Smoothness,Optical performance,High anti-blocking,Food contact compliance
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.922	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	3.5	g/10min	ISO 1133

film	Nominal value	Unit
film thickness
test	38	µm
film thickness	0.020mm to 0.040 mm

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	90.0	℃	ISO 306/A
Melting temperature	110	℃	ISO 11357-3

optical performance	Nominal value	Unit	Test method
gloss
45°，38 µm	65		ASTM D2457
Haze
38 µm	2.5	%	ASTM D2457

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	43		ISO 868
tensile strength			ISO 527-2
yield	10.0	MPa	ISO 527-2
fracture	12.0	MPa	ISO 527-2
Tensile strain
fracture	600	%	ISO 527-2
friction coefficient			ISO 8295
With oneself – dynamic	< 0.11		ISO 8295
With oneself – static	< 0.11		ISO 8295

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	145 to 165	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.