| About |
|---|
| NORYL FP3060 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and high flow , this resin also uses non-chlorinated, non-brominated FR additives to achieve a V1 UL94 rating at 1.5 mm and V0@ 2.5mm with a specific density of 1.1 g/cm^3. NORYL FP3060 may be an excellent material candidate for Flat Panel TV enclosure applications requiring good rheological properties, heat resistance, hydrolysis resistance, low density and thin wall flame resistance.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,High liquidity,Hydrolysis stability,Halogen free,Flame Characteristics,High Heat Resistance,Low density,V-1,V-0 |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Flow Rate | |||
| 200℃，3.80kg | 42 | g/10min | ASTM D1238 |
| Melt Volume Rate | ISO 1133 | ||
| 300℃，1.2 kg | 20.0 | cm³/10min | |
| 280℃，2.16 kg | 41.0 | cm³/10min | |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.13 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.020 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 2200 | MPa | ASTM D638 |
| — | 2420 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 54.0 | MPa | ASTM D638 |
| yield | 55.0 | MPa | ISO 527-2/50 |
| fracture | 55.0 | MPa | ASTM D638 |
| fracture | 42.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 3.0 | % | ASTM D638 |
| yield | 3.0 | % | ISO 527-2/50 |
| fracture | 12 | % | ASTM D638 |
| fracture | 11 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 2400 | MPa | ASTM D790 |
| — | 2530 | MPa | ISO 178 |
| bending strength | |||
| — | 82.0 | MPa | ISO 178 |
| Yield, 50 mm span | 84.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6.0 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 78 | J/m | ASTM D256 |
| -30℃ | 5.0 | kJ/m² | ISO 180-1A |
| 23℃ | 6.0 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 80.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 74.0 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| — | 105 | ℃ | ASTM D1525 14 |
| B50 | 91.0 | ℃ | ISO 306 |
| B120 | 93.0 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | ASTM E831, ISO 11359-2 | ||
| MD：-40~40℃ | 8.3E-5 | 1/℃ | |
| TD：-40~40℃ | 8.0E-5 | 1/℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-1 | ||
| 2.50 mm | V-0 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 65.0 to 75.0 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Hopper temperature | 60.0 to 80.0 | °C | |
| Barrel rear temperature | 200 to 220 | °C | |
| Barrel middle temperature | 230 to 260 | °C | |
| Barrel front temperature | 250 to 285 | °C | |
| Nozzle temperature | 240 to 270 | °C | |
| Processing (melt) temperature | 250 to 285 | °C | |
| Mold temperature | 40.0 to 65.0 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*4 sp=62mm |
| 8. 80*10*4 mm |
| 9. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |