| About |
|---|
| Loyblend® TY-1000 is high impact compounded blend of polycarbonate and polybtylene terephathalate. This grade offers good chemical resistance, good dimensional stability and high heat resistance.&& |
| Product Description | |
|---|---|
| Generic | PC+PBT |
| Material Status | Commercial: Active |
| Features | High impact resistance,Good Dimensional Stability,High Heat Resistance,Solvent resistance,HB |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.21 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 20 | g/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| TD | 0.60 to 1.0 | % | |
| MD | 0.60 to 1.0 | % | |
| Water absorption rate | ISO 62 | ||
| 23℃，24hr | 0.080 | % | |
| Saturation, 23 ℃ | 0.30 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2150 | MPa | ISO 527-1-2 |
| tensile strength | ISO 527-2/50 | ||
| yield | 65.0 | MPa | |
| fracture | 60.0 | MPa | |
| Tensile strain | |||
| fracture | > 100 | % | ISO 527-2/50 |
| Bending modulus | 2300 | MPa | ISO 178 |
| bending strength | 90.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 50 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 700 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 110 | ℃ | ISO 75-2/A |
| Continuous use temperature | 90.0 | ℃ | IEC 60216 |
| Vicat Softening Temp | |||
| A50 | 140 | ℃ | ISO 306/A50 |
| Ball pressure test | |||
| 125℃ | Pass | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| MD：-30~30℃ | 8.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 3 mm | 18 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | |||
| Solution A | 200 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 | |
| Glowing wire flammability index | |||
| 2.0 mm | 650 | ℃ | IEC 60695-2-12 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | |||
| — | 110 | °C | |
| Pre-drying equipment | 110 to 120 | °C | |
| Drying time | |||
| — | 2.0 | hr | |
| Pre-drying equipment | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 240 to 280 | °C | |
| Mold temperature | 80.0 to 110 | °C | |
| Injection speed | 中等 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |