| About |
|---|
| 2103-65D is a thermoplastic polyurethane elastomer. Feature: Low temperature impact&& |
| Product Description | |
|---|---|
| Supplier | Lubrizol Advanced Materials |
| Generic | TPU-醚 |
| Material Status | Commercial: Active |
| Features | low-temperature impact resistance |
| Availabilitys | North America,Latin America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.17 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 224℃，5.0kg | 35 | g/10min | ASTM D1238 |
| Shrinkage rate | ASTM D955 | ||
| MD | 0.50 to 0.90 | % | |
| TD | 0.60 to 1.0 | % | |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| Fracture, 3.20 mm | 39.6 | MPa | ASTM D412 |
| 50% strain, 3.20 mm | 17.2 | MPa | |
| 100% strain, 3.20 mm | 19.3 | MPa | |
| 300% strain, 3.20 mm | 33.1 | MPa | |
| Tensile strain | |||
| Fracture, 3.20 mm | 360 | % | ASTM D412 |
| tear strength | |||
| 3.20 mm | 193 | kN/m | ASTM D624 |
| Compression deformation | ASTM D395B | ||
| 25℃，22 hr | 30 | % | |
| 70℃，22 hr | 35 | % |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 117 | ℃ | ASTM D1525 2 |
| Linear coefficient of thermal expansion | |||
| MD | 1.3E-4 | 1/℃ | ASTM D696 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 64 | ASTM D2240 | |
| Bending modulus | |||
| 3.20 mm | 231 | MPa | ASTM D790 |
| Taber abraser | |||
| 1000 g, H-22 wheel | 90.0 | mg | ASTM D1044 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 99.0 to 110 | °C | |
| Processing (melt) temperature | 210 to 221 | °C | |
| Mold temperature | 16.0 to 60.0 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 3. Rate B (120°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |