| Separated-type liquid epoxy resin Application : Ignition coil package Advantage : Good impregnation ability&& |
| Product Description | |
|---|---|
| Supplier | SBHPP |
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Water absorption rate | |||
| 2HR, in water | 0.2 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Bending modulus | |||
| 25℃ | 8500 | MPa | |
| bending strength | |||
| 25℃ | 110 | MPa |
| Thermosetting mixed viscosity | Nominal value | Unit | Test method |
|---|---|---|---|
| 60℃ | 500 | cP | ASTM D2393 |
| Uncured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | |||
| 25℃ | 1.70 | g/cm³ |
| Cured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 90 | ||
| Volume resistivity | |||
| 25 ℃ | 1.0E+16 | ohms·cm | |
| Breakdown voltage (1.00 mm) | 33 | kV/mm |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 120 | ℃ | TMA |
| Linear coefficient of thermal expansion | |||
| MD | 4.0E-5 | 1/℃ | TMA |
| Thermosetting components | |||
| Component A | 按重量计算的混合比: 100 | ||
| Component B | 按重量计算的混合比: 100 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |