| About |
|---|
| GP100ORXP is a High Density Polyethylene compound specially developed for the manufacturing of extruded pipes for gas distribution. It is produced with bimodal technology and has high molar mass. It shows excellent mechanical properties and resistance to hydrostatic pressure and stress cracking. This resin has MRS (Minimum Required Strength) of 10 MPa, according to ISO 9080, and is classified as PE 100, according to ISO 12162. GP100ORXP is manufactured in orange color and contains additives to protect it against ultraviolet radiation action and photodegradation. Meets the requirements of NBR 14462:00 and ISO 4437:07. Application: Orange PE 100 pressure pipes for gas distribution; jacketing of underwater cables Process: Pipe Extrusion.&& |
| Product Description | |
|---|---|
| Supplier | Braskem |
| Generic | HDPE |
| Material Status | Commercial: Negative |
| Features | Weather resistance is good,High molecular weight,Bimodal molecular weight distribution,High ESCR |
| Availabilitys | Latin America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.948 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，5.0kg | 0.25 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | ASTM D1693 | ||
| 50 ℃, 2.00 mm, 10% non-ionic surfactant, molded, F50 | > 1000 | hr | ASTM D1693 |
| 50 ℃, 2.00 mm, 100% non-ionic surfactant, molded, F50 | > 1000 | hr | ASTM D1693 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| Compression Molding | 无断裂 | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, molded | 69.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 125 | ℃ | ASTM D1525 2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 64 | ASTM D2240 | |
| tensile strength | ASTM D638 | ||
| Yield, molding | 24.0 | MPa | ASTM D638 |
| Fracture, molded | 38.0 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| Yield, molding | 10 | % | ASTM D638 |
| Fracture, molded | 1500 | % | ASTM D638 |
| Bending modulus | |||
| 1% cut, molded | 1050 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |