| CYCOLOY CY6025 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) resin is a standard grade that can be injection molded. This non-chlorinated, non-brominated flame retardant PC/ABS has a UL V0 & 5VB flame rating. CYCOLOY CY6025 resin is a general purpose resin that is an excellent candidate for a wide variety of thin wall applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | High liquidity,Halogen free,Flame Characteristics,V-1,V-0,5VB |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Flow Rate | |||
| 260℃，2.16kg | 28 | g/10min | ASTM D1238 |
| Shrinkage rate | Internal Method | ||
| MD | 0.23 | % | |
| TD | 0.31 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.29 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 59.0 | MPa | Internal Method |
| yield | 56.0 | MPa | ASTM D638 |
| yield | 57.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 79 | % | Internal Method |
| fracture | 99 | % | ASTM D638 |
| fracture | 99 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 2570 | MPa | ASTM D790 |
| — | 2880 | MPa | ISO 178 |
| bending strength | |||
| — | 96.0 | MPa | ISO 178 |
| Yield, 50 mm span | 89.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 11 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 370 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 64 mm span | 83.6 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.2 mm | 72.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 74.0 | ℃ | ISO 75-2/Af |
| Linear coefficient of thermal expansion | ASTM E831 | ||
| MD：-40~40℃ | 7.0E-5 | 1/℃ | |
| TD：-40~40℃ | 6.7E-5 | 1/℃ | |
| Relative temperature index | 60.0 | ℃ | UL 746 |
| Electrical performance | 60.0 | ℃ | UL 746 |
| Impact mechanical performance | 60.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+15 | ohms | ASTM D257 |
| Compared to the leakage tracing index | PLC 0 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.00 mm | V-1 | ||
| 1.20 mm | V-0 | ||
| 1.50 mm | 5VB |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82.2 to 87.8 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.040 | % | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 2.0 in/min |
| 3. 0.051 in/min |
| 4. 0.079 in/min |
| 5. at Yield |
| 6. 80*10*3 sp=62mm |
| 7. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |