| About |
|---|
| Zenite 6330L is a lubricated 30% mineral-reinforced LCP resin having excellent toughness. It is well suited for use in the automotive, electrical/electronic, telecommunications, and aerospace industries.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | 液态聚合物 |
| Material Status | Commercial: Active |
| Features | Good flexibility,Lubricating |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.63 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.50 | % | ISO 294-4 |
| MD | 0.0 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 10500 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| fracture | 125 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 4.0 | % | ISO 527-2/1A/5 |
| Bending modulus | |||
| 23℃ | 9600 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 125 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 239 | ℃ | ISO 75-2/A |
| Melting temperature | 335 | ℃ | ISO 11357-3 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 150 | °C | |
| Drying time | 3.0 | hr | |
| Recommended maximum moisture content | 0.010 | % | |
| Hopper temperature | 20 to 30 | °C | |
| Barrel rear temperature | 335 to 345 | °C | |
| Barrel middle temperature | 350 to 360 | °C | |
| Barrel front temperature | 350 to 360 | °C | |
| Nozzle temperature | 350 to 360 | °C | |
| Processing (melt) temperature | 350 to 360 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Injection pressure | 50.0 to 150 | MPa | |
| Hold pressure | 50.0 to 150 | MPa | |
| Back pressure | 0.00 to 3.00 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |