| About |
|---|
| Visico LE4421M / Visico LE4431M is a two-part silane crosslinkable insulation system, specially designed for insulation applications. Applications Visico LE4421M / Visico LE4431M is intended for insulation of XLPE medium voltage cables with rated voltages up to 36 kV. Specifications Visico LE4421M / Visico LE4431M in combination meets the applicable requirements as below when processed using sound extrusion and testing procedure: IEC 60502-2 Cenelec HD620 S2 The standards referred to above is a selection and is not complete coverage of all applicable standards. Contact your Borealis representative for additional information. Special Features Visico LE4421M / Visico LE4431M is a ready-to-use two part system. It provides the following advantages: Quick change-over for short length cables Long shelf life Longer production runs between cleaning stops Low odour during processing Very good surface finish&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | PE |
| Material Status | Commercial: Active |
| Features | High impact resistance,High Heat Resistance,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 50 ℃, 10% non-ionic surfactant, F20 | > 96.0 | hr | IEC 60811-4-1/B |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 1 second | 52 | ISO 868 | |
| tensile strength | > 15.0 | MPa | ISO 527-2/250 |
| Tensile strain | |||
| fracture | > 300 | % | ISO 527-2/250 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -76.0 | ℃ | ASTM D746 |
| thermosetting | IEC 60811-2-1 | ||
| Elongation under load: 200 ℃ | 60 | % | IEC 60811-2-1 |
| Permanent deformation: 200 ℃ | 0.0 | % | IEC 60811-2-1 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Mechanical properties of air oven after aging | |||
| 135 ℃, 240 hr, rate of change in tensile strength | < -75 | % | IEC 60811 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric strength | > 22 | kV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 50 Hz | < 2.30 | IEC 60250 | |
| Dissipation factor | |||
| 50 Hz | < 5.0E-4 | IEC 60250 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Mixture 95:5 |
| 3. Base Resin |
| 4. 0.20 MPa |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |