| Grilamid® L 25 G nat 6011 is a Polyamide 12 (Nylon 12) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for extrusion or film extrusion. Important attributes of Grilamid® L 25 G nat 6011 are: RoHS Compliant Food Contact Acceptable High Viscosity Mold Release Agent Typical applications include: Film Food Contact Applications Packaging&& |
| Product Description | |
|---|---|
| Supplier | EMS-GRIVORY |
| Generic | PA12 |
| Material Status | Commercial: Active |
| Features | High Viscosity,Food contact compliance,Lubricating |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 275℃，5 kg | 20.0 | cm³/10min | ISO 1133 |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 1.5 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.70 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1600 | MPa | ISO 527-2 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ISO 527-3 | ||
| MD, yield | 35.0 | MPa | ISO 527-3 |
| TD, yield | 35.0 | MPa | ISO 527-3 |
| MD, fracture | 80.0 | MPa | ISO 527-3 |
| TD, fracture | 70.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, yield | 6.0 | % | ISO 527-3 |
| TD, yield | 6.0 | % | ISO 527-3 |
| MD, fracture | 850 | % | ISO 527-3 |
| TD, fracture | 900 | % | ISO 527-3 |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD | 10 | N | ISO 6383-2 |
| TD | 10 | N | ISO 6383-2 |
| Pant tear resistance | ISO 6383-1 | ||
| MD | 20.0 | N/mm | ISO 6383-1 |
| TD | 25.0 | N/mm | ISO 6383-1 |
| Water vapor transmittance | |||
| 23℃，85% RH | 8.0 | g/m²/24 hr | DIS 15106-1/-2 |
| Oxygen transfer rate | DIS 15105-1/-2 | ||
| 23℃ | 350 | cm³/m²/bar/24 hr | DIS 15105-1/-2 |
| 23℃ | 370 | cm³/m²/bar/24 hr | DIS 15105-1/-2 |
| Carbon dioxide transfer rate | DIS 15105-1/-2 | ||
| 23℃ | 1500 | cm³/m²/bar/24 hr | DIS 15105-1/-2 |
| 23℃ | 1600 | cm³/m²/bar/24 hr | DIS 15105-1/-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | — | kJ/m² | ISO 179/1eA |
| 23℃ | — | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Continuous use temperature | |||
| — | 80.0 to 110 | ℃ | ISO 2578 |
| — | 150 | ℃ | Internal Method |
| Melting temperature | 178 | ℃ | ISO 11357-3 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Gelboflextest | 1300 | holes/m² | Internal Method |
| ISO Type | PA 12, E, 24-010 | ISO 1874 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0% RH |
| 3. 85% RH |
| 4. Long Term |
| 5. Short Term |
| 6. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |