| Versaflex™ OM 6258-9 是专门设计用于粘接多种标准和改性过的尼龙材料，包括 那些经过玻璃填充、热稳定处理和/或冲击性改进的材料 。 新产品。还未建立商业规范。 着色能力极强 在二次或嵌件注射成型过程中粘结性极佳 柔软，手握时类似于橡胶 非常容易加工&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | TPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good bond,Good coloring,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Shore hardness | |||
| 10 seconds | 62 | ASTM D2240 | |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| Fracture, 23 ℃ | 2.76 | MPa | ASTM D412 |
| 100% strain, 23 ℃ | 1.90 | MPa | ASTM D412 |
| 300% Strain, 73°F | 2.65 | MPa | ASTM D412 |
| Tensile strain | |||
| Fracture, 23 ℃ | 350 | % | ASTM D412 |
| tear strength | 18.6 | kN/m | ASTM D624 |
| Compression deformation | |||
| 23℃，22 hr | 23 | % | ASTM D395B |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 1.4 to 2.0 | % | ASTM D955 |
| Apparent viscosity of melt | |||
| 200℃，11200 sec^-1 | 31.6 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Proposed maximum recycled material ratio | 20 | % | |
| Barrel rear temperature | 182 to 204 | °C | |
| Barrel middle temperature | 243 to 266 | °C | |
| Barrel front temperature | 249 to 271 | °C | |
| Nozzle temperature | 254 to 277 | °C | |
| Processing (melt) temperature | 249 to 271 | °C | |
| Mold temperature | 13 to 29 | °C | |
| Back pressure | 0.00 to 0.552 | MPa | |
| Screw speed | 80 to 120 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |